The slump test is the most well-known and widely used test method to characterize the workability of fresh concrete. The inexpensive test, which measures consistency, is used on job sites to determine rapidly whether a concrete batch should be accepted or rejected. The test method is widely standardized throughout the world, including in ASTM C143 in the United States and EN 12350-2 in Europe.
The apparatus consists of a mold in the shape of a frustum of a cone with a base diameter of 8 inches, a top diameter of 4 inches, and a height of 12 inches. The mold is filled with concrete in three layers of equal volume. Each layer is compacted with 25 strokes of a tamping rod. The slump cone mold is lifted vertically upward and the change in height of the concrete is measured.
Four types of slumps are commonly encountered, as shown in Figure 3. The only type of slump permissible under ASTM C143 is frequently referred to as the “true” slump, where the concrete remains intact and retains a symmetric shape. A zero slump and a collapsed slump are both outside the range of workability that can be measured with the slump test. Specifically, ASTM C143 advises caution in interpreting test results less than ½ inch and greater than 9 inches. If part of the concrete shears from the mass, the test must be repeated with a different sample of concrete. A concrete that exhibits a shear slump in a second test is not sufficiently cohesive and should be rejected.
The apparatus consists of a mold in the shape of a frustum of a cone with a base diameter of 8 inches, a top diameter of 4 inches, and a height of 12 inches. The mold is filled with concrete in three layers of equal volume. Each layer is compacted with 25 strokes of a tamping rod. The slump cone mold is lifted vertically upward and the change in height of the concrete is measured.
Four types of slumps are commonly encountered, as shown in Figure 3. The only type of slump permissible under ASTM C143 is frequently referred to as the “true” slump, where the concrete remains intact and retains a symmetric shape. A zero slump and a collapsed slump are both outside the range of workability that can be measured with the slump test. Specifically, ASTM C143 advises caution in interpreting test results less than ½ inch and greater than 9 inches. If part of the concrete shears from the mass, the test must be repeated with a different sample of concrete. A concrete that exhibits a shear slump in a second test is not sufficiently cohesive and should be rejected.
The slump test is not considered applicable for concretes with a maximum coarse aggregate size greater than 1.5 inches. For concrete with aggregate greater than 1.5 inches in size, such larger particles can be removed by wet sieving.
Additional qualitative information on the mobility of fresh concrete can be obtained after reading the slump measurement. Concretes with the same slump can exhibit different behavior when tapped with a tamping rod. A harsh concrete with few fines will tend to fall apart when tapped and be appropriate only for applications such as pavements or mass concrete. Alternatively, the
concrete may be very cohesive when tapped, and thus be suitable for difficult placement conditions.
Additional qualitative information on the mobility of fresh concrete can be obtained after reading the slump measurement. Concretes with the same slump can exhibit different behavior when tapped with a tamping rod. A harsh concrete with few fines will tend to fall apart when tapped and be appropriate only for applications such as pavements or mass concrete. Alternatively, the
concrete may be very cohesive when tapped, and thus be suitable for difficult placement conditions.
Slump is influenced by both yield stress and plastic viscosity; however, for most cases the effect of plastic viscosity on slump is negligible. Equations have been developed for calculating yield stress in terms of slump, based on either analytical or experimental analyses. Since different rheometers measure different absolute values for the yield stress of identical samples of concrete, the experimental equations are largely depended on the specific device used to measure yield stress.
Advantages: • The slump test is the most widely used device worldwide. In fact, the test is so well known that often the terms workability and slump are used interchangeably, even though they have different meanings.
• Specifications are typically written in terms of slump.
• The slump test is simple, rugged, and inexpensive to perform. Results are obtained immediately.
• The results of the slump test can be converted to yield stress in fundamental units based on various analytical treatments and experimental studies of the slump test.
• Compared to other commonly used concrete tests, such as for air content and
compressive strength, the slump test provides acceptable precision.
Disadvantages:
• The slump test does not give an indication of plastic viscosity.
• The slump test is a static, not dynamic, test; therefore, results are influenced by concrete thixotropy. The test does not provide an indication of the ease with which concrete can be moved under dynamic placing conditions, such as vibration.
• The slump test is less relevant for newer advanced concrete mixes than for more conventional mixes.